New degradation mechanism observed for AlGaN/GaN HEMTs with sub 100 nm scale unpassivated regions around the gate periphery
P. Ivoa, E.M. Choa, P. Kotaraa , L. Schellhasea, R. Lossya, U. Zeimera, A. Mogilatenkoa, J. Würfla, G. Tränklea, A. Glowackib, C. Boitb
Published in:
Microelectron. Reliab., vol. 54, no. 6-7, pp. 1288-1292 (2014).
Abstract:
AlGaN/GaN HEMTs with low gate leakage current in the µA/mm range have been fabricated with a small- unpassivated region close to the gate foot. They showed considerably higher critical voltage values (average VCR = 60 V) if subjected to step stress testing at OFF-state conditions and room temperature as com- pared to standard devices with conventional gate technology. This is due to the fact that electrons injected from the gate can be accumulated at the unpassivated region and thus builds up negative charge. The lower gate leakage is due to virtual gate formation, which is reducing local electric field in the vicinity of the gate. In contrast to devices with standard gate technology, degradation during step stressing is not associated with a simultaneous gate leakage and drain leakage current increase but with a strong increase of drain current at OFF-state conditions while the gate leakage is practically not affected. Then a relatively higher critical voltage of around 60 V is achieved. An abrupt increase of subthreshold drain current implies the formation of a conductive channel bypassing the gate region without influencing gate leakage. It is believed that hopping conductivity via point defects formed during device stressing creates this channel. Once this degradation mode takes place, the drain current of affected devices significantly drops. This can be explained by negative trap formation in the channel region affecting the total charge balance in 2DEG region. Electroluminescence measurements on both fresh and degraded devices showed no hot spots at OFF-state conditions. However, there is additional emission at ON-state bias, which sug- gests additional energetic states that lead to radiative electron transition effects in the degraded devices, most possibly defect states in the buffer.
a Ferdinand-Braun-Institut, Leibniz-Institut für Höchstfrequenztechnik, Gustav-Kirchhoff-Straße 4, D-12489 Berlin, Germany
b Halbleiterbauelemente Technische Universität Berlin, Einsteinufer 19, 10589 Berlin, German
Keywords:
GaN reliability, Electroluminescence
Copyright © 2014 Elsevier Ltd. All rights reserved.. Personal use of this material is permitted. However, permission to reprint/republish this material for advertising or promotional purposes or for creating new collective works for resale or redistribution to servers or lists, or to reuse any copyrighted component of this work in other works must be obtained from the Elsevier Ltd.