F. Brunner¹, J.-T. Zettler² and M. Weyers¹

Published in:

Semicond. Sci. Technol., vol. 33, no. 4, pp. 045014 (2018).

Abstract:

An extensive analysis of the degradation characteristics of AlGaN-based ultraviolet light-emitting diodes emitting around 265 nm is presented. The optical power of LEDs stressed at a constant dc current of 100mA (current density=67 A/cm² and heatsink temperature=20°C) decreased to about 58% of its initial value after 250 h of operation. The origin of this degradation effect has been studied using capacitance-voltage and photocurrent spectroscopy measurements conducted before and after aging. The overall device capacitance decreased, which indicates a reduction of the net charges within the space-charge region of the pn-junction during operation. In parallel, the photocurrent at excitation energies between 3.8 eV and 4.5 eV and the photocurrent induced by band-to-band absorption in the quantum barriers at 5.25 eV increased during operation. The latter effect can be explained by a reduction of the donor concentration in the active region of the device. This effect could be attributed to the compensation of donors by the activation or diffusion of acceptors, such as magnesium dopants or group-III vacancies, in the pn-junction space-charge region. The results are consistent with the observed reduction in optical power since deep level acceptors can also act as non-radiative recombination centers.

Copyright © 2018 IOP Publishing Ltd. Personal use of this material is permitted. However, permission to reprint/republish this material for advertising or promotional purposes or for creating new collective works for resale or redistribution to servers or lists, or to reuse any copyrighted component of this work in other works must be obtained from the IOP Publishing Ltd.

Full version in pdf-format.