H. Wenzel, G. Erbert, F. Bugge, A. Knauer, J. Maege, J. Sebastian, R. Staske, K. Vogel, G. Tränkle

Published in:

Proc. SPIE, vol. 3947, pp. 32-39 (2000).

Abstract:

Tensile strained GaAsP quantum wells (QWs) embedded in AlGaAs waveguide and cladding layers are an alternative approach for the wavelength range 700-800 nm. We will present a detailed experimental and theoretical study of the dependence of the threshold current on the thickness and the strain of the QW for 800 nm. The optimum thickness of the GaAsP QW for a minimum threshold current density is about 14 nm and is thus much larger than for compressively strained QWs. Higher characteristic temperatures T₀ can be obtained with even thicker QWs. In order to achieve high optical output powers and good fiber coupling efficiencies, we used broad waveguides with weak optical confinement and small far field divergence. We prepared two structures with 1µm thick Al_0.65Ga_0.35As (structure A) and 2µm thick Al_0.45Ga_0.55As (structure b) waveguides, respectively. For structure B, the thickness of the Al_0.70Ga_0.30As cladding layers must be carefully optimized in order to suppress higher-order tranverse modes. Whereas structure B yields a higher maximum cw output power of AR/HR coated broad-area devices, structure A shows a better high-temperature behavior. Aging tests performed at 2 W (100 µm stripe width) and 25°C suggest a very good reliability of these devices.

© 2000 SPIE-The International Society for Optical Engineering. Personal use of this material is permitted. However, permission to reprint/republish this material for advertising or promotional purposes or for creating new collective works for resale or redistribution to servers or lists, or to reuse any copyrighted component of this work in other works must be obtained from the SPIE.

Full version in pdf-format.