M. Pristovsek, M. Zorn , M. Weyers

Published in:

Journal of Crystal Growth 262 (2004) 78-83.

Abstract:

A comparative study of GaAs (001) growth from tri-methyl gallium (TMGa) and tri-ethyl gallium (TEGa) was performed in metal-organic vapour phase epitaxy. The growth surfaces were characterised by reflectance anisotropy spectroscopy (RAS). Three distinct shapes of the RAS spectra typical for certain growth parameter regions were observed for both precursors. The RAS spectra typical for the growth at low temperatures correspond to kinetic limited growth and the surface is covered by adsorbates. At slightly higher temperatures in mass transport limited growth mode, a more gallium-rich surface appears with both precursors. In the case of TEGa, the lack of arsenic on the surface below 500°C is simply due to the lack of decomposed AsH₃. However, using TMGa gallium-rich surfaces are already found below 600°C. We propose steric hindrance of As diffusion by methyl groups around the incorporation sites and forced arsenic desorption by the formation of methyl arsine as the cause. At typical buffer growth temperatures above 600°C, the surfaces during growth are identical to the AsH₃, stabilised arsenic-rich pre-growth surfaces for both gallium precursors.

Keywords:
A1. Reflection anisotropy spectroscopy; A1. Growth models; A3. Metalorganic vapor phase epitaxy; B2. Semiconducting gallium arsenide

© 1999-2003, Elsevier Science B.V.. Personal use of this material is permitted. However, permission to reprint/republish this material for advertising or promotional purposes or for creating new collective works for resale or redistribution to servers or lists, or to reuse any copyrighted component of this work in other works must be obtained from the Elsevier Science B.V.

Full version in pdf-format.