O. Krüger¹, T. Wernicke¹, J. Würfl¹, R. Hergenröder², G. Tränkle¹

Published in:

Appl. Phys. A, vol. 93, no. 1, pp. 85-91 (2008).

Abstract:

The effects of direct UV laser processing on single crystal SiC in ambient air were investigated by crosssectional transmission electron microscopy, Auger electron spectroscopy, and measurements of the electrical resistance using the transfer length method (TLM). Scanning electron microscopy was applied to study the morphology and dimensions of the laser-treated regions. After laser processing using a nanosecond pulsed solid-state laser the debris consisting of silicon oxide was removed by etching in buffered hydrofluoric acid. A layer of resolidified material remains at the surface indicating the thermal impact of the laser process. The Si/C ratio is significantly disturbed at the surface of the resolidified layer and approaches unity in a depth of several tens of nanometers. A privileged oxidation of carbon leaves elementary resolidified silicon at the surface, where nanocrystalline silicon was detected. Oxygen and nitrogen were detected near the surface down to a depth of some tens of nanometers. A conductive surface film is formed, which is attributed to the thermal impact causing the formation of the silicon-rich surface layer and the incorporation of nitrogen as dopant. No indications for microcrack or defect formation were found beneath the layer of resolidified material.

PACS:

68.37.Lp, 79.20.Ds, 81.40.-z, 81.70.Jb

Copyright © 2008, Springer Berlin / Heidelberg. Personal use of this material is permitted. However, permission to reprint/republish this material for advertising or promotional purposes or for creating new collective works for resale or redistribution to servers or lists, or to reuse any copyrighted component of this work in other works must be obtained from the Springer-Verlag.

Full version in pdf-Format.